Utilization of Blast Furnace Solid Waste (Slag) As Cement Substitution Material on Mortar Manufacture

Jurnal Riset Teknologi Pencegahan Pencemaran Industri

View Publication Info
 
 
Field Value
 
Title Utilization of Blast Furnace Solid Waste (Slag) As Cement Substitution Material on Mortar Manufacture
 
Creator Amin, Muhammad
Isnugroho, Kusno
Hendronursito, Yusup
 
Subject slag
substitution
cement
physical test
compressive strength
material
 
Description Slag is defined as a waste material produced from iron ore smelting process in blast furnace. The slag was derived from Research Center for Mineral Technology located in Tanjung Bintang Lampung Selatan with particle size of 80,100, and 120 mesh. The percentages of slag used as cement substitution were 10%, 20%, and 30% from total volume. Test pieces was made by compressing all mixture material in 50 x 50 x 50 mm cubical mortar mold. Physical test of mortars, such as : porosity test, density test and compressive strength test were performed. Based on physical test of samples, it was shown that the higher ratio of slag used in cement substitution gives higher mortar porosity. Substitution of 10% slag with size of 100 mesh produced the porosity of 3.45%, while the substitution 20% and 30% slag with the same size, produced 5.08% and 5.76% porosity, compared with the standard of mortar which was 5.12%. The compressive strength test with 10% slag substitution was 19.3 Mpa, while 20% substitute slag gave the compressive strength of 19.1 Mpa and 30% substitute slag has compressive strength value of 18.7 Mpa. The standard mortar is 17.2 Mpa. However, beside of slag substitution ratio, the slag particle size also affected the compressive strength and porosity. Based on the results explained, the substitution of slag as a substitute for cement in mortar strength was still above the mortar standard.
 
Publisher Balai Besar Teknologi Pencegahan Pencemaran Industri
 
Date 2020-05-15
 
Type info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
Peer-reviewed Article
 
Format application/pdf
 
Identifier http://jrtppi.id/index.php/jrtppi/article/view/59
10.21771/jrtppi.2018.v9.no1.p22-28
 
Source Jurnal Riset Teknologi Pencegahan Pencemaran Industri; Vol. 9 No. 1 (2018); 22-28
2503-5010
2087-0965
10.21771/jrtppi.2018.v9.no1
 
Language eng
 
Relation http://jrtppi.id/index.php/jrtppi/article/view/59/52
 
Rights Copyright (c) 2018 Balai Besar Teknologi Pencegahan Pencemaran Industri
http://creativecommons.org/licenses/by/4.0/
 

Contact Us

The PKP Index is an initiative of the Public Knowledge Project.

For PKP Publishing Services please use the PKP|PS contact form.

For support with PKP software we encourage users to consult our wiki for documentation and search our support forums.

For any other correspondence feel free to contact us using the PKP contact form.

Find Us

Twitter

Copyright © 2015-2018 Simon Fraser University Library