Pengaruh Komposisi Pasir Cetak Terhadap Mutu Cetakan Pasir Coran Aluminium

Jurnal Teknik Mesin

View Publication Info
 
 
Field Value
 
Title Pengaruh Komposisi Pasir Cetak Terhadap Mutu Cetakan Pasir Coran Aluminium
 
Creator Bukhari, Bukhari
Nofriadi, Nofriadi
Yanziwar, Yanziwar
 
Description Casting is a manufacturing procces that use mold and molten metal to make parts. Geometry of the mold is almost same with the product. Shape of sand mold is negative shape of product that according to desire pattern. Making procces of mold must following right composition of sand mold. After through some test, strength of sand mold is depand on composition of mater. Value of the test on table 1 (89% sand, 9% water glass, and 2% water, has tensile strength 0,66 N/mm2 ) and compared to table 3. (85% sand, 9% water glass dan 2% water, has tensile strength 0,415 N/mm2 ). Based on the test, mold with 100% new sand has better collapse is mold with composition 94% new sand, 4% water glass, 2% water, has tensile strength 0,417 N/mm2, but, muld with 50% new sand 50% recycle sand has better collapse is mold with composition 45% new sand, 45% recycle sand, 6% water glass, and 4% water, has tensile strength 0,474 N/mm2.
 
Publisher Politeknik Negeri Padang
 
Date 2019-12-31
 
Type info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
 
Format application/pdf
 
Identifier http://ejournal2.pnp.ac.id/index.php/jtm/article/view/227
10.30630/jtm.12.2.227
 
Source Jurnal Teknik Mesin; Vol 12 No 2 (2019): Jurnal Teknik Mesin; 50-54
2655-5670
1829-8958
 
Language eng
 
Relation http://ejournal2.pnp.ac.id/index.php/jtm/article/view/227/136
 
Rights Copyright (c) 2019 Jurnal Teknik Mesin
 

Contact Us

The PKP Index is an initiative of the Public Knowledge Project.

For PKP Publishing Services please use the PKP|PS contact form.

For support with PKP software we encourage users to consult our wiki for documentation and search our support forums.

For any other correspondence feel free to contact us using the PKP contact form.

Find Us

Twitter

Copyright © 2015-2018 Simon Fraser University Library