SINTESIS LAPISAN TIPIS (THIN FILM) SnO2 DAN SnO2:Al MENGGUNAKAN TEKNIK SOL-GEL SPIN COATING PADA SUBSTRAT KACA DAN QUARTZ

Jurnal Penelitian Pendidikan IPA (JPPIPA)

View Publication Info
 
 
Field Value
 
Title SINTESIS LAPISAN TIPIS (THIN FILM) SnO2 DAN SnO2:Al MENGGUNAKAN TEKNIK SOL-GEL SPIN COATING PADA SUBSTRAT KACA DAN QUARTZ
 
Creator Imawanti, Yanika Diah
Doyan, Aris
Gunawan, Erin Ryantin
 
Description This study has successfully synthesized SnO2 and SnO2 thin films by doping aluminum (Al) using the technique of sol-gel spin coating on glass and quartz substrates. The basic materials are Tin (II) chloride dihydrate (SnCl2.2H2O) and ethanol (C2H5OH) as solvent.  Material for doping is AlCl3 as much as 0.027 g, 0.053 g and 0.08 g to get Al dopant concentration of 5%, 10% and 15% respectively. The substrate used in this study are glass and quartz with the dimension of 10 mm x 10 mm x 3 mm. Detergent water, distilled water and 70% alcohol were used for the preparation of the substrates. Pure SnO2 sol solution was obtained by dissolving SnCl2.2H2O in ethanol, and SnO2:Al was obtained by adding AlCl3 to the solution of SnO2. The stirring process was done by using a hot plate magnetic stirrer to obtained a homogeneous solution (transparent). Sol solution of pure SnO2 and SnO2:Al were allowed for 24 hours as maturation (aging) process. Solution deposition on a substrate was done with a rotary speed of 2000 rpm for 3 minutes. Heating process was done at the annealing temperature of 200°C to 400°C by using a furnace for 1 hour to grow the crystalline of thin films. This thin films are very appropriate when applied to transparent conductive oxide (TCO) materials with high transparency and conductive character of tin (Sn) and aluminum (Al)Keyword: SnO2‚ aluminum‚ sol-gel, spin coating, substrate
 
Publisher Universitas Mataram
 
Contributor
 
Date 2017-01-31
 
Type info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion

 
Format application/pdf
 
Identifier http://jppipa.unram.ac.id/index.php/jppipa/article/view/49
10.29303/jppipa.v3i1.49
 
Source Jurnal Penelitian Pendidikan IPA; Vol 3, No 1 (2017): January
2407-795X
2460-2582
10.29303/jppipa.v3i1
 
Language eng
 
Relation http://jppipa.unram.ac.id/index.php/jppipa/article/view/49/48
 
Rights Copyright (c) 2017 Jurnal Penelitian Pendidikan IPA
 

Contact Us

The PKP Index is an initiative of the Public Knowledge Project.

For PKP Publishing Services please use the PKP|PS contact form.

For support with PKP software we encourage users to consult our wiki for documentation and search our support forums.

For any other correspondence feel free to contact us using the PKP contact form.

Find Us

Twitter

Copyright © 2015-2018 Simon Fraser University Library